含钪黑钨渣酸浸液中锆的N235+TBP预萃取

金属矿山 ›› 2016, Vol. 45 ›› Issue (09): 112-116.

含钪黑钨渣酸浸液中锆的N235+TBP预萃取

丁冲¹，刘秀^2,3，王晓辉²，单志强¹，张新海¹，何超然^2,3

1.中国有色桂林矿产地质研究院有限公司，广西桂林 541004；2.湿法冶金清洁生产技术国家工程实验室，北京 100190；3.中国矿业大学(北京)化学与环境工程学院，北京 100083

出版日期:2016-09-15 发布日期:2016-10-18
基金资助:
基金项目国家自然科学基金项目(编号：51474199)。

N235+TBP Preextraction of Zr from Wolframine Residue Containing Sc

Ding Chong¹，Liu Xiu^2,3，Wang Xiaohui²，Shan Zhiqiang¹，Zhang Xinhai¹，He Chaoran^2,3

1.CNMC Guilin Research Institute of Geology for Mineral Resources，Guilin 541004，China；2.National Engineering Lab.of Hydrometallurgy Cleaner Production Technology,Beijing 100190,China；3.School of College of Chemistry and Environmental Engineering，China University of Mining and Technology(Beijing)，Beijing 100083,China

Online:2016-09-15 Published:2016-10-18

摘要/Abstract

摘要： 湖南某黑钨渣硫酸浸出液（硫酸的浓度为1.8 mol/L）的钪、锆元素含量分别为48.18、138.00 mg/L，为消除锆对萃取钪的影响，在萃取钪前以N235和TBP为复合萃取剂进行了除锆预萃取试验。结果表明：①在复合萃取剂N235、TBP与磺化煤油的体积比为15∶15∶70，有机相与水相相比为1.5∶1，萃取时间为5 min，萃取温度为25 ℃，萃取振荡频率为120 r/min情况下进行单级萃取，对应的锆、钪萃取率分别为92.03%和0.96%；在硫酸溶液浓度为5 mol/L、反萃相比为3∶1、反萃时间为30 min、反萃温度为25 ℃、振荡频率为180 r/min情况下进行3级反萃，对应的锆、钪反萃率分别为99.23%和98.22%。因此，该工艺可高效地分离锆、钪。②再生有机相对萃原液中锆的萃取率可达91.97%，与新配制萃取剂效果接近，说明再生萃取剂可以循环利用。

关键词: 钪, 锆, N235, TBP, 萃取, 反萃

Abstract: The content of Sc and Zr is 48.18 mg/L and 138.00 mg /L respectively in sulfuric acid leaching solution(sulfuric acid concentration 1.8 mol/L) of some wolframine slag from Hunan.To eliminate the effect of Zr on Sc extraction,zirconium pre removal experiment using N235 and TBP as composite extracting agent was conducted before scandium extraction.Results show that：①Under the condition of volume ratio of N235，TBP and sulfonated kerosene is 15∶15∶70 in the composite extracting agent，ratio of organic phase to water phase 1.5∶1，extraction time 5 min，extraction temperature 25 ℃，extraction oscillation frequency 120 r/min，single stage extraction was conducted and extraction rates of Zr and Sc were 92.03% and 0.96% respectively.Under the condition of sulfuric acid solution concentration 5 mol/L，the ratio of organic phase to water phase of extraction 3∶1，reverse extraction time 30 min，reverse extraction temperature 25 ℃，oscillation frequency 180 r/min，three-levels reverse extraction was conducted and extraction rates of Zr and Sc were 99.23% and 98.22% respectively.Therefore，the process can efficiently separate zirconium and scandium.②Extraction rate of Zr can reach to 91.97% by regenerative extractant whose effect is close to the new extractant，which illustrates regenerative extractant can be recycled.

Key words: Sc, Zr, N235, TBP, Extraction, Reextraction

丁冲, 刘秀, 王晓辉, 单志强, 张新海, 何超然. 含钪黑钨渣酸浸液中锆的N235+TBP预萃取[J]. 金属矿山, 2016, 45(09): 112-116.

DING Chong, LIU Xiu, WANG Xiao-Hui, DAN Zhi-Qiang, ZHANG Xin-Hai, HE Chao-Ran. N235+TBP Preextraction of Zr from Wolframine Residue Containing Sc[J]. Metal Mine, 2016, 45(09): 112-116.

[1]	邓善芝, 程仁举, 李成秀, 刘星. 甘肃某含钪低品位钛铁矿石综合利用试验[J]. 金属矿山, 2019, 48(05): 69-73.
[2]	陈玥, 张承龙, 邓明强, 马恩　王瑞雪, 王景伟. 离子液体［C16mim］［NTf₂］萃取H₂SO₄-NaClO₃溶液体系中的Au（Ⅲ）[J]. 金属矿山, 2019, 48(03): 116-118.
[3]	谌纯, 张一敏, 黄晶, 包申旭, 杨晓. 高浓度盐酸体系下叔胺N235三相萃取钒试验[J]. 金属矿山, 2017, 46(05): 99-103.
[4]	韩朗, 庹必阳. 锆柱撑蒙脱石对铜离子的吸附效果[J]. 金属矿山, 2017, 46(05): 177-180.
[5]	张一敏, 包申旭. 含钒浸出液净化富集技术现状及前景[J]. 金属矿山, 2016, 45(07): 64-70.
[6]	宋炯, 覃小锋, 张晓华, 王宗起, 韩小宾. 梵净山地区燕山期流纹斑岩的发现及地质意义[J]. 金属矿山, 2014, 43(09): 103-107.
[7]	闫国强, 丁俊, 黄勇, 王欣欣, 张凯. 西藏山南比马组安山岩形成时代及意义[J]. 金属矿山, 2014, 43(08): 91-94.
[8]	郝文彬, 戴子林, 郭秋松, 危青, 李云霄. 石煤直接酸浸提钒富液铵盐沉钒工艺研究[J]. 金属矿山, 2014, 43(06): 75-78.
[9]	凌小明, 赵晓东, 李军敏, 吕涛. 车盘向斜南东翼铝土矿钪特征及综合利用前景[J]. 金属矿山, 2014, 43(01): 88-91.
[10]	王一, 张一敏, 黄晶, 刘涛, 李望, 张国斌. 石煤酸浸提钒浸出液萃取试验研究[J]. 金属矿山, 2013, 42(03): 100-103.
[11]	秦红, 薛伟, 解田, 金洋华, 张仁忠. 某钼镍钒多金属矿石镍钒浸出液萃钒试验[J]. 金属矿山, 2013, 42(02): 90-93.
[12]	曹钊, 曹永丹, 李解, 屈启龙, 王介良. 稀土金属及其共生铌的湿法冶金技术现状[J]. 金属矿山, 2013, 42(01): 97-100.
[13]	周吉奎, 胡洁. 生化浸出—萃取—电积提取废弃线路板中铜[J]. 金属矿山, 2012, 41(12): 136-139.
[14]	唐平宇, 王素, 周建国, 庞玉荣. 从碎云母尾矿中回收铁及独居石锆石的选矿试验[J]. 金属矿山, 2012, 41(10): 153-156+168.
[15]	高玉德, 韩兆元, 王国生. 朝鲜某复杂难选钽铌锆矿选矿试验研究[J]. 金属矿山, 2012, 41(07): 91-94.