金属矿山 ›› 2016, Vol. 45 ›› Issue (12): 89-93.

黑沟铁矿石粉矿（-15 mm）棒磨磨矿工艺试验

王明星¹，李艳军¹，刘金长²，李文博¹

1.东北大学资源与土木工程学院，辽宁沈阳 110819；2.甘肃省难选铁矿石资源利用重点实验室，甘肃嘉峪关 735100

出版日期:2016-12-15 发布日期:2017-02-16
基金资助:
基金项目：中央高校基本科研业务费项目（编号:N150103003)。

Research on Rod-grinding Technology of Heigou Iron Ore Fines (-15 mm)

Wang Mingxing¹，Li Yanjun¹，Liu Jinzhang²，Li Wenbo¹

1.School of Resources and Civil Engineering，Northeastern University，Shenyang 110819，China；2.Gansu Provincial Key Laboratory of Refractory Iron Ore Resource Utilization，Jiayuguan 735100，China

Online:2016-12-15 Published:2017-02-16

摘要/Abstract

摘要： 黑沟铁矿石粉矿（-15 mm）铁品位为37.35%，铁主要以赤褐铁矿形式存在，铁在赤褐铁矿中分布率为85.35%。现场采用球磨机磨矿后强磁选工艺回收粉矿，球磨机磨矿时泥化现象严重，细粒级铁矿物无法通过强磁选有效回收。为减轻粉矿磨矿过程的过粉碎现象，优化磨矿产品粒度组成，对破碎至-2 mm的粉矿，预选筛分出产率为33.30%的-120 μm粒级，对+120 μm粒级进行棒磨机磨矿试验。在棒径分别为18、20、22 mm的钢棒为磨矿介质，且其质量比为4∶3∶3、介质充填率为30%、料棒比为1.0、磨矿浓度为70%、磨矿时间为62 s条件下闭路磨矿，合格粒级（38~120 μm）占-120 μm粒级比例达57.55%。降低分级粒度能够有效减少微细粒级的产生，减少过磨。采用棒磨工艺可以减少过磨，优化磨矿产品的粒度组成。

关键词: 欠磨, 过磨, 棒磨, 闭路磨矿

Abstract: Iron grade of fines（-15 mm） iron ore from Heigou is 37.35%.Iron mainly exists in form of hematite-limonite and the distribution rate is 85.35%.The fines iron ore was recovered by high intensity magnetic separation after ball milling in on-site process，while sliming phenomenon in grinding operation is serious，the fines iron ore can′t be recovered by high intensity magnetic separation.In order to relieve over crushing phenomenon during grinding and optimize size composition of grinding products.The fines were crushed to -2 mm，Pre-screened -120 μm size fraction with the rate of 33.30%.Rod milling experiments were implemented for +120 μm size fraction.Closed-circuit grinding was carried out with the conditions that grinding medium of rod diameter 18，20，22 mm with mass ratio of 4∶3∶3，medium filling ratio of 30%，rod to powder ratio 1.0，grinding concentration 70% and grinding for 62 s，and it can obtain qualified size fraction (38~120 μm) accounts for 57.55% of -120 μm size fraction.Decreasing classification particle size can reduce production of fine particle effectively and over grinding.It has a significant reference to reducing over grinding and optimize the size composition of grinding products by rod milling technology.

Key words: Lack grinding, Over grinding, Rod grinding, Closed circuit grinding

王明星, 李艳军, 刘金长, 李文博. 黑沟铁矿石粉矿（-15 mm）棒磨磨矿工艺试验[J]. 金属矿山, 2016, 45(12): 89-93.

WANG Ming-Xing, LI Yan-Jun, LIU Jin-Chang, LI Wen-Bo. Research on Rod-grinding Technology of Heigou Iron Ore Fines (-15 mm)[J]. Metal Mine, 2016, 45(12): 89-93.

[1]	李强常永强王荣生曾繁森. 提高某微细粒铅锌矿选锌指标的试验研究[J]. 金属矿山, 2021, 50(05): 96-102.
[2]	韦寒波, 高谦 . 废石—棒磨砂混合充填料浆工作特性与流变参数试验[J]. 金属矿山, 2020, 49(12): 55-60.
[3]	李茂辉, 陈志杰, 高谦. 基于棒磨砂充填料的新型充填胶凝材料优化决策[J]. 金属矿山, 2018, 47(02): 64-69.
[4]	耿伟利, 罗天明, 郭文军. 我国细粒铅锌矿浮选技术现状及发展[J]. 金属矿山, 2015, 44(03): 116-119.
[5]	张发明, 林日孝, 管则皋, 王洪岭, 郑少冰. 大陆槽稀土矿石磁浮联合选矿工艺研究[J]. 金属矿山, 2014, 43(10): 98-102.
[6]	王永定. 金川矿山混合充填材料配比试验[J]. 金属矿山, 2014, 43(09): 16-20.
[7]	曹学鹏, 喻连香, 周吉奎, 顾帼华. 某高岭土矿石中黄铁矿的分选试验[J]. 金属矿山, 2014, 43(06): 177-180.
[8]	杜浩荣, 杨波, 朱运凡, 刘杰. 提高会泽铅锌矿选矿回收率方法探讨[J]. 金属矿山, 2013, 42(01): 101-103.
[9]	白镇河, 何方威, 李世国, 吴晓元, 陈忠基. 旋流器-格子型球磨机一段闭路磨矿分级的研究[J]. 金属矿山, 2008, 38(05): 103-105+109.

扫码分享