胶结充填采矿协同资源化利用垃圾焚烧飞灰固化机理研究

金属矿山 ›› 2018, Vol. 47 ›› Issue (03): 196-200.

胶结充填采矿协同资源化利用垃圾焚烧飞灰固化机理研究

杨恒^1,2,3，倪文^1,2,3，马旭明^1,2,3，高巍^1,2,3，许成文^1,2,3，巴浩静^1,2,3

1.北京科技大学土木与环境工程学院，北京 100083；2.金属矿山高效开采与安全教育部重点实验室，北京100083；3.工业典型污染物资源化处理北京市重点实验室，北京100083

出版日期:2018-03-15 发布日期:2018-03-20

Study on the Mechanism of Synergistic Utilization of Fly Ash from Solid Waste Incineration by Cemented Filling Mining

Yang Heng^1,2,3，Ni Wen^1,2,3，Ma Xuming^1,2,3，Gao Wei^1,2,3，Xu Chengwen^1,2,3，Ba Haojing^1,2,3

1.School of Civil and Environment Engineering，University of Science and Technology Beijing，Beijing 100083，China；2.Key Laboratory of High-efficient Mining and Safety of Metal Mines，Ministry of Education，Beijing 100083，China；3.Key Laboratory of Resource-oriented Treatment of Industrial Pollutants，Beijing 100083，China

Online:2018-03-15 Published:2018-03-20

摘要/Abstract

摘要： 为确定低成本、安全、高效处置危废城市垃圾焚烧飞灰(MSWI)的方法，以钢渣微粉、矿渣粉、脱硫石膏、垃圾焚烧飞灰和尾砂为充填材料，进行了砂浆流动性能和胶结充填料强度试验，根据胶结充填料强度确定了胶凝材料的最优配比，并通过X射线衍射（XRD），红外（FTIR）和扫描电镜(SEM)分析了净浆试块的微观结构和水化产物。试验结果表明，当垃圾焚烧飞灰掺量为15%、钢渣微粉掺量为4%、脱硫石膏掺量为14%、矿渣粉掺量为67%时，料浆的流动度为260 mm，满足自流型胶结充填的流动性需求，充填料试块28 d的抗压强度为24.54 MPa，满足矿山充填强度要求；充填料试块养护28 d重金属离子浸出浓度全部低于饮水标准；冶金渣-垃圾焚烧飞灰胶凝材料水化产物主要有钙矾石、C—S—H凝胶和Friedel盐。

关键词: 垃圾焚烧飞灰, 全固废, 胶结充填, 矿渣

Abstract: In order to determine the research method of low-cost，safe and efficient disposal of municipal solid waste incineration fly ash (MSWI)，we conducted the flow performance and strength test of filling material which were made of slag powder，slag powder，gypsum，incineration fly ash.The optimal mixing ratio of cementitious material was determined according to the strength of cement filler.The microstructure and hydration products of the cement paste were analyzed by X-ray diffraction (XRD)，infrared (FTIR) and scanning electron microscopy (SEM).The results show that when the content of waste incineration fly ash is 15%，the content of steel slag is 4%，the content of desulphurization gypsum is 14% and the slag content is 67%，the fluidity of the slurry is 260 mm，which satisfies the liquidity requirement of the self-flow cementation filling，and the compressive strength of the filling material is 24.54 MPa for 28 days，which satisfies the requirement of filling strength of the mine.The leaching concentration of heavy metal ions for 28 days was all lower than that of drinking water.The hydration products of Metallurgical slag-incineration fly ash cementing material are mainly ettringite，C-S-H gel and Friedel salt.

Key words: Waste incineration fly ash, All solid waste, Cementation filling,Slag

杨恒, 倪文, 马旭明, 高巍, 许成文, 巴浩静. 胶结充填采矿协同资源化利用垃圾焚烧飞灰固化机理研究[J]. 金属矿山, 2018, 47(03): 196-200.

YANG Heng, NI Wen, MA Xu-Ming, GAO Wei, XU Cheng-Wen, BA Hao-Jing. Study on the Mechanism of Synergistic Utilization of Fly Ash from Solid Waste Incineration by Cemented Filling Mining[J]. Metal Mine, 2018, 47(03): 196-200.

[1]	梁秋群, 刘峥, 梁楚欣, 杨瑞善, 张淑芬. 高岭土/锰尾矿渣-秸秆复合保温材料的制备及其性能研究[J]. 金属矿山, 2020, 49(09): 214-220.
[2]	程爱平, 董福松, 戴顺意, 舒鹏飞, 付子祥. 全尾砂胶结充填体分层特性试验研究[J]. 金属矿山, 2020, 49(08): 13-19.
[3]	于恩毅, 黄旭东, 王珍岐, 黄晢航, 龚甲桂 . 废石掺量对胶结充填体强度及变形破坏的影响[J]. 金属矿山, 2020, 49(08): 44-48.
[4]	石满生, 许威, 张美道, . 基于 Rhino-Griddle-Flac3D的矿体建模与地表稳定性分析[J]. 金属矿山, 2020, 49(08): 182-187.
[5]	吴振坤, 金爱兵, 陈帅军 . 胶结充填体动力试验及其爆破响应模拟研究[J]. 金属矿山, 2020, 49(07): 25-32.
[6]	赵奎, 卓毓龙, 曾鹏, 王万银. 下向分层胶结充填开采中的协同性[J]. 金属矿山, 2020, 50(05): 19-25.
[7]	迟晓鹏, 郭芸杉, 衷水平, 吕旭龙, 刘春, 吴健辉. 新型捕收剂GC-I在铜矿渣浮选中的应用[J]. 金属矿山, 2020, 50(05): 205-209.
[8]	程爱平, 张玉山, 董福松, 戴顺意. 考虑空隙非线性变形的胶结充填体损伤软化本构模型研究[J]. 金属矿山, 2019, 48(08): 13-21.
[9]	杜惠惠, 倪文, 高广军, 徐东, 张思奇. 钒钛矿渣制备全固废胶凝材料的初步研究[J]. 金属矿山, 2019, 48(08): 192-197.
[10]	程爱平, 董福松, 张玉山, 王平, 戴顺意. 胶结充填体波速-密度双参数强度预测模型研究[J]. 金属矿山, 2019, 48(07): 26-31.
[11]	王一杰, 李克庆, 倪文, 张思奇, 李佳. 矿渣基胶凝材料固化垃圾焚烧飞灰中重金属的研究[J]. 金属矿山, 2019, 48(07): 194-198.
[12]	李茂辉, 陈志杰. 某低活性酸性矿渣微粉的机械力化学效应研究[J]. 金属矿山, 2019, 48(03): 200-204.
[13]	侯晨, 朱万成, 张洪训, 郭良银, 杜加法, 刘晓光. 胶结充填体与矿柱相互作用双轴加载试验研究[J]. 金属矿山, 2019, 48(01): 24-28.
[14]	鄢琪慧, 倪文, 高巍, 李云云, 张钰莹. 矿渣-钢渣基胶凝材料固化某含砷尾砂试验[J]. 金属矿山, 2018, 47(11): 189-192.
[15]	杨昊, 王志强, 詹炳根. 脱硫灰渣的改性及其对矿渣基充填料性能的影响研究[J]. 金属矿山, 2018, 47(11): 193-196.