镜铁矿悬浮磁化焙烧过程中的铁物相与磁性转变研究

金属矿山 ›› 2019, Vol. 48 ›› Issue (02): 38-43.

镜铁矿悬浮磁化焙烧过程中的铁物相与磁性转变研究

李嘉^1,2，孙永升^1,2，李艳军^1,2，韩跃新^1,2

1. 东北大学资源与土木工程学院，辽宁沈阳 110819；2. 难采选铁矿资源高效开发利用技术国家地方联合工程研究中心，辽宁沈阳 110819

出版日期:2019-02-25 发布日期:2019-04-08
基金资助:
基金项目：国家自然科学基金项目（编号： 1874071）。

Study on Iron Phase Transformation and Magnetic Transformation during Suspension Magnetization Roasting of Specularite

Li Jia^1,2， Sun Yongsheng^1,2， Li Yanjun^1,2， Han Yuexin^1,2

1. School of Resources and Civil Engineering， Northeastern University， Shenyang 110819， China；2. National-Local Joint Engineering Research Center of Refractory Iron Ore Resources Efficient Utilization Technology，Shenyang 110819, China

Online:2019-02-25 Published:2019-04-08

摘要/Abstract

摘要： 甘肃某镜铁矿石主要有价元素为铁，TFe含量为59.61%，原矿中94.79%的铁以赤褐铁的形式存在，脉石矿物主要为石英，含量为8.11%。为考察焙烧过程主要影响因素对焙烧产物的物相转化与磁性转变的影响，进行了悬浮焙烧试验。结果表明：镜铁矿经悬浮磁化焙烧后，焙烧产物中铁主要以磁铁矿的形式存在，磁性明显增强；随着焙烧温度升高、焙烧时间延长、CO浓度增加、总气量增加，焙烧产品中镜铁矿含量均逐渐降低，磁铁矿含量均逐渐增加，焙烧产品饱和磁化强度和最大比磁化系数均先提高后降低；在焙烧温度为550 ℃、焙烧时间为4 min、CO浓度为20%、总气量为600 mL/min时，焙烧产物的比饱和磁化强度为63.66 A·m²/kg、最大比磁化系数为5.02×10-4 m³/kg；焙烧过程铁物相按照Fe₂O₃→Fe₃O₄→FeO的反应顺序进行，焙烧产物铁物相的转化会影响铁矿物磁性的强弱，并且主要与磁铁矿的含量相关。试验结果可以为我国镜铁矿资源悬浮焙烧过程机理研究提供理论依据。

关键词: 镜铁矿, 悬浮磁化焙烧, 物相转化, 磁性转变

Abstract: The main valuable element of a specularite ore in Gansu Province is iron. The content of TFe is 59.61%. 94.79% of the iron in the raw ore exists in the form of hematite and limonite. The gangue mineral is mainly quartz and the content is 8.11%. In order to investigate the effect of main factors on phase transformation and magnetic transformation of roasted products， suspension roasting experiments were carried out. The results show that after the suspension magnetization roasting of specularite， the roasted product iron mainly exists in the form of magnetite， and the magnetism is obviously enhanced. With the increase of roasting temperature， roasting time， CO concentration and total gas volume， the content of specularite in roasted products decreases gradually， the content of magnetite increases gradually， and the saturation magnetization and maximum specific magnetization coefficient of roasted products increase first and then decrease. The specific saturation magnetization of the roasted product is 63.66 A·m²/kg and the maximum specific magnetization coefficient is 5.02×10-4 m³/kg when the roasting temperature is 550 ℃ and the roasting time is 4 min， the concentration of CO is 20% and the total gas volume is 600 mL/min. The iron phase in the roasting process changes in the order of Fe₂O₃→Fe₃O₄→FeO. The transformation of the phase of the roasted product will affect the magnetic strength， and is mainly related to the content of magnetite. The experimental results can provide theoretical basis for the mechanism of suspension roasting of specularite resources in China.

Key words: Specularite, Suspension magnetization roasting, Phase transformation, Magnetism transformation

李嘉, 孙永升, 李艳军, 韩跃新. 镜铁矿悬浮磁化焙烧过程中的铁物相与磁性转变研究[J]. 金属矿山, 2019, 48(02): 38-43.

LI Jia, SUN Yong-Sheng, LI Yan-Jun, HAN Yue-Xin. Study on Iron Phase Transformation and Magnetic Transformation during Suspension Magnetization Roasting of Specularite[J]. Metal Mine, 2019, 48(02): 38-43.

[1]	孙洪硕, 陈毅琳, 韩跃新, 王建雄, 高泽宾, 李嘉. 酒钢铁矿石悬浮磁化焙烧试验及机理研究[J]. 金属矿山, 2022, 51(04): 96-101.
[2]	张强, 孙永升, 韩跃新, 李艳军, 高鹏. 悬浮磁化焙烧—氧化冷却过程中磁赤铁矿生成规律[J]. 金属矿山, 2022, 51(02): 102-109.
[3]	王若枫 , 袁帅 , 高鹏, 李艳军 , 孙永升. 高铁铝土矿悬浮磁化焙烧铁铝分离技术研究[J]. 金属矿山, 2021, 50(04): 113-118.
[4]	杨任新, 董亚宁, 李明阳, 童雄, 高翔鹏, 刘军 . 霓石、镜铁矿晶体各向异性及粒度差异对可浮性的影响[J]. 金属矿山, 2020, 49(12): 101-107.
[5]	陈毅琳, 唐晓玲, 李艳军, 刘金长, 孙永升. 酒钢尾矿悬浮磁化焙烧扩大连续试验研究[J]. 金属矿山, 2020, 50(05): 178-184.
[6]	李明阳, 陈泽, 胡义明, 刘军, 张颖异, 高翔鹏. 霓石溶出金属离子对镜铁矿、霓石可浮性的影响[J]. 金属矿山, 2019, 48(04): 53-57.
[7]	唐晓玲, 陈毅琳, 韩跃新, 李艳军, 刘金长. 酒钢粉矿悬浮磁化焙烧扩大试验研究[J]. 金属矿山, 2019, 48(02): 29-33.
[8]	马玉成, 李艳军, 孙永升. 酒钢镜铁矿悬浮磁化焙烧试验研究[J]. 金属矿山, 2019, 48(02): 34-37.
[9]	周立波, 李文博, 徐瑞清, 韩跃新. 鞍钢东部尾矿资源特征及磁选预富集工艺研究[J]. 金属矿山, 2018, 47(11): 176-180.
[10]	崔进兵, 陈铁军, 胡佩伟. 镜铁矿磁化焙烧试验及其焙烧产品磁性研究[J]. 金属矿山, 2018, 47(10): 63-69.
[11]	马玉新, 白丽梅, 侯宇, 邓玉芬, 刘淑贤. 新疆某镜铁矿石磁化焙烧过程研究[J]. 金属矿山, 2017, 46(06): 75-79.
[12]	赖伟强. 山西某低品位含金镜铁矿选矿试验[J]. 金属矿山, 2017, 46(06): 94-98.
[13]	袁帅, 韩跃新, 高鹏, 李艳军, 孙永升. 难选铁矿石悬浮磁化焙烧技术研究现状及进展[J]. 金属矿山, 2016, 45(12): 9-12.
[14]	屈万刚, 陈铁军, 张一敏. 0~1 mm镜铁矿制粒—磁化焙烧—弱磁选试验[J]. 金属矿山, 2016, 45(02): 61-65.
[15]	苏涛, 陈铁军, 汪博. 甘肃某镜铁矿尾矿磁化焙烧—弱磁选试验[J]. 金属矿山, 2015, 44(02): 173-176.