煤系高岭土低温煅烧降低COD增加有序度试验

金属矿山 ›› 2013, Vol. 42 ›› Issue (09): 91-93+116.

煤系高岭土低温煅烧降低COD增加有序度试验

田钊¹，张凌燕¹，管俊芳¹，杨泽清^2,3，黎晓松³，刘新¹，曹刚¹

1.武汉理工大学资源与环境工程学院；2.湖北柳树沟矿业股份有限公司；3.湖北宜昌兴山亮特精粉有限公司

出版日期:2013-09-16 发布日期:2013-11-22

Experimental Research on Low-temperature Calcination of Coal-series Kaolin to Reduce the COD and Improve the Order Degree

Tian Zhao¹，Zhang Lingyan¹，Guan Junfang¹，Yang Zeqing ^2,3，Li Xiaosong³，Liu Xin¹，Cao Gang¹

1.School of Resource and Environmental Engineering，Wuhan University of Technology；2.Hubei Liushugou Mining Co.，Ltd.；3.Xingshan Liangte Kaolin-powder Industry Co.，Ltd. of Yichang，Hubei

Online:2013-09-16 Published:2013-11-22

摘要/Abstract

摘要： 对湖北兴山某COD值较高的煤系高岭土进行了低温煅烧试验研究。结果表明，在425 ℃情况下煅烧0.5 h，COD值可从1.005 6×10-2降至2.523×10-3，满足玻璃纤维用高岭土对COD值的要求。煅烧前后产品的XRD和红外图谱对比分析表明：低温煅烧不仅能有效去除高岭土原料中绝大部分的有机质，降低产品的COD值，还能有效地保存原料中绝大部分的结构水，确保玻纤配料的活性和微区搅拌功能，同时提高产品的有序度。

关键词: 煤系高岭土, 低温煅烧, COD, 有序度

Abstract: A low-temperature calcination test of coal-series Kaolin with high COD from Xingshan of Hubei Province was studied. The results showed that the COD value was reduced from 1.0056×10-2 to 2.523×10-3 when the kaolin was roasted for 0.5 h at 425 ℃，which met the requirement of glass fiber for kaolin on COD. Contrasting and analyzing the XRD and IR spectra of product before and after calcinations，it is showed that low-temperature calcination not only could remove most of organic material from kaolin to reduce the COD value，but also can effectively save the vast constitution water in kaolin，which could ensure the activity of glass fiber material and the mixing function of micro area，and moreover improve the order degree of product.

Key words: Coal-series kaolin, Low-temperature calcination, COD, Order degree

田钊, 张凌燕, 管俊芳, 杨泽清, 黎晓松, 刘新, 曹刚. 煤系高岭土低温煅烧降低COD增加有序度试验[J]. 金属矿山, 2013, 42(09): 91-93+116.

TIAN Zhao, ZHANG Ling-Yan, GUAN Jun-Fang, YANG Ze-Qing, LI Xiao-Song, LIU Xin, CAO Gang. Experimental Research on Low-temperature Calcination of Coal-series Kaolin to Reduce the COD and Improve the Order Degree[J]. Metal Mine, 2013, 42(09): 91-93+116.

[1]	张金山, 周珊, 李侠, 范雯阳, 邹东雪, 孙春宝. 用内蒙古煤系高岭土制备NaY分子筛[J]. 金属矿山, 2016, 45(04): 164-168.
[2]	朱晓丽, 陈瑞军, 幺琳, 吴占兴. 铁尾矿陶粒的制备及对生活污水的处理[J]. 金属矿山, 2015, 44(08): 178-180.
[3]	伍泽广, 石松林, 刘钦甫. 煤系高岭土制备微孔硅酸钙[J]. 金属矿山, 2011, 40(01): 162-164.
[4]	杜小满, 刘钦甫, 邢楠, 张金山, 程宏飞. 煅烧煤系高岭土和硅粉用于混凝土的对比试验[J]. 金属矿山, 2010, 39(09): 170-172,187.
[5]	米丽平, 孙春宝, 周峰, 孙体昌. 某铜铅锌硫化矿浮选废水特性研究[J]. 金属矿山, 2010, 39(05): 161-164.
[6]	李向明, 璩世杰, 李光华, 张会林, 许文耀. 台阶炮孔爆破软件BLAST-CODE及其在歪头山铁矿的应用[J]. 金属矿山, 2008, 38(12): 51-54.
[7]	王萍, 李国昌. 粉煤灰陶粒滤料的制备及在生物滤池中的应用研究[J]. 金属矿山, 2008, 38(11): 114-117.

扫码分享