酒钢-1 mm镜铁矿粉矿微波磁化焙烧—弱磁选试验

金属矿山 ›› 2014, Vol. 43 ›› Issue (12): 66-69.

酒钢-1 mm镜铁矿粉矿微波磁化焙烧—弱磁选试验

马浩¹，陈铁军^1,2，刘伟¹，黄献宝¹，苏涛¹，屈万刚¹

1.武汉科技大学资源与环境工程学院，湖北武汉 430081；2.冶金矿产资源高效利用与造块湖北省重点实验室，湖北武汉 430081

出版日期:2014-12-15 发布日期:2015-07-23

Experiment of the Process of Microwave Magnetization Roasting and Low Intensity Magnetic Separation for Fine Specularite at -1 mm of Jiugang

Ma Hao¹，Chen Tiejun^1,2，Liu Wei¹，Huang Xianbao¹，Su Tao¹，Qu Wan'gang¹

1.College of Resource and Environment Engineering，Wuhan University of Science and Technology，Wuhan 430081，China；2.Hubei Key Laboratory for Efficient Utilization and Agglomeration of Metallurgic Mineral Resources，Wuhan 430081，China

Online:2014-12-15 Published:2015-07-23

摘要/Abstract

摘要： 鉴于酒钢-1 mm镜铁矿粉矿采用常规选矿方法难以获得好的分选指标，进行常规磁化焙烧—弱磁选又需解决球团问题，以哈密烟煤为还原剂，对该粉矿开展了微波磁化焙烧—弱磁选研究，考察了煤粉用量、微波功率、焙烧温度、焙烧时间、焙烧产品磨矿细度和弱磁选磁场强度对所获铁精矿指标的影响。试验结果表明，在煤粉与矿石的质量比为5%、微波功率为1 kW、焙烧温度为550 ℃条件下将该粉矿微波磁化焙烧15 min，然后将焙烧矿磨细至-0.074 mm占85.65%，在92.16 kA/m磁场强度下进行1次磁选管选别，可获得铁精矿铁品位为55.10%、铁回收率为86.65%的较好指标，从而为该-1 mm镜铁矿粉矿中铁矿物的高效回收提供了一种新思路。

关键词: 酒钢-1 mm镜铁矿粉矿, 微波磁化焙烧, 弱磁选

Abstract: It is hard to obtain good separation index for the specularite at -1 mm in Jiugang company by conventional beneficiation process.In the conventional magnetic roasting-low intensity magnetic separation，the problem of pellets has to be solved.With Hami bituminous coal as reducing agent，the process of the microwave magnetization roasting-low intensity magnetic separation study for fine ore is carried out to investigate the effect of the dosage of pulverized coal，microwave power，roasting temperature，roasting time，grinding fineness of roasted products and low intensity magnetic field strength on the iron concentrate indexes.The test results showed that under the conditions of the mass ratio of pulverized coal to ore 5%，microwave power 1 kW，and calcined at 550 ℃，the raw fine ores were treated by the microwave magnetizing roasting for 15 min，and then the roasted products are ground to the fineness of -0.074 mm 85.65%.By this method，good indicators of iron concentrate with Fe grade of 55.10% and Fe recovery of 86.65% was achieved by adopting one-stage magnetic tube separation with magnetic field strength of 92.16 kA/m.The research provides a new idea for high efficient recovery of iron ore from fine specularite at -1 mm.

Key words: -1 mm fine specularite of Jiusteel, Microwave magnetizing roasting, Low intensity magnetic separation

马浩, 陈铁军, 刘伟, 黄献宝, 苏涛, 屈万刚. 酒钢-1 mm镜铁矿粉矿微波磁化焙烧—弱磁选试验[J]. 金属矿山, 2014, 43(12): 66-69.

MA Hao, CHEN Tie-Jun, LIU Wei, HUANG Xian-Bao, SU Tao, QU Wan-Gang. Experiment of the Process of Microwave Magnetization Roasting and Low Intensity Magnetic Separation for Fine Specularite at -1 mm of Jiugang[J]. Metal Mine, 2014, 43(12): 66-69.

[1]	田小松, 武立伟, 赵　洵, 梁泽跃, 戴惠新, 吕玉辰, 王飞旺. 缅甸某低品位复杂难选铁锡矿石综合回收试验研究[J]. 金属矿山, 2024, 53(4): 135-.
[2]	刘旭 , 孙永升 , 祝昕冉 , 韩跃新. 包子铺褐铁矿石微波悬浮磁化焙烧技术研究[J]. 金属矿山, 2023, 52(04): 92-96.
[3]	张剑廷杨峰李志明房舜尧. 马钢姑山铁矿石磁化焙烧—弱磁选试验研究[J]. 金属矿山, 2022, 51(11): 101-106.
[4]	杨光, 马自飞 , 杨会利 , 袁立宾, 孙永升 . 东鞍山铁矿石高效分选新技术研究[J]. 金属矿山, 2021, 50(08): 88-94.
[5]	曹丽英, 刘文凯, 汪建新, 张逸, 任明明, 孔令辉. 新型干式磁选机分选品位影响因素试验研究[J]. 金属矿山, 2020, 49(09): 197-201.
[6]	刘军, 牟景春, 李庚辉, 张永, 张春田. 南芬混合铁矿石的可磨性研究与选矿工艺优化[J]. 金属矿山, 2019, 48(09): 71-77.
[7]	周咏, 田艳红. 研山铁矿综合尾矿再选试验及生产实践[J]. 金属矿山, 2019, 48(05): 188-191.
[8]	邓善芝, 程仁举, 李成秀, 刘星. 甘肃某含钪低品位钛铁矿石综合利用试验[J]. 金属矿山, 2019, 48(05): 69-73.
[9]	王静静, 曹志成, 高建勇, 颜坤. 某高镁低铁镍型红土镍矿石转底炉法还原提镍试验[J]. 金属矿山, 2019, 48(03): 90-94.
[10]	何威, 曾维伟, 陈向, 廖德华. 某菱铁矿石直接还原—弱磁选试验[J]. 金属矿山, 2019, 48(03): 86-89.
[11]	董振海, 李文博, 李艳军. 辽西风化壳型钒钛磁铁矿预富集试验研究[J]. 金属矿山, 2019, 48(02): 150-155.
[12]	郭文达, 韩跃新, 朱一民, 李艳军, 范志国. 岩浆岩型含钛铁精矿降钛研究[J]. 金属矿山, 2019, 48(02): 71-75.
[13]	马玉成, 李艳军, 孙永升. 酒钢镜铁矿悬浮磁化焙烧试验研究[J]. 金属矿山, 2019, 48(02): 34-37.
[14]	闫克勤. 贵州某锂辉石矿石选矿试验[J]. 金属矿山, 2018, 47(11): 95-97.
[15]	刘军, 丁开振, 王炬. 罗河铁矿选矿工艺流程优化[J]. 金属矿山, 2018, 47(03): 116-121.

扫码分享