石煤焙烧—加压酸浸提钒研究

金属矿山 ›› 2015, Vol. 44 ›› Issue (10): 85-89.

石煤焙烧—加压酸浸提钒研究

黄俊^1,2，张一敏^1,2,3，黄晶^1,2，刘涛^1,2，薛楠楠^1,2

1.武汉科技大学资源与环境工程学院，湖北武汉 430081；2.湖北省页岩钒资源高效清洁利用工程技术研究中心，湖北武汉430081；3.钒资源高效利用湖北省协同创新中心，湖北武汉 430081

出版日期:2015-10-15 发布日期:2015-11-20
基金资助:
基金项目国家自然科学基金项目(编号：51404174)。

Study on Roasting-Pressure Acid Leaching of Vanadium from Stone Coal

Huang Jun^1,2，Zhang Yimin^1,2,3，Huang Jing1^,2，Liu Tao1^,2，Xue Nannan1^,2

1.School of Resources and Environmental Engineering，Wuhan University of Science and Technology，Wuhan 430081，China；2.Hubei Provincial Engineering Technology Research Center of High Efficient Cleaning Utilization for Shale Vanadium Resource，Wuhan 430081，China；3.Hubei Provincial Collaborative Innovation Center for High Efficient Utilization of Vanadium Resources，Wuhan 430081，China

Online:2015-10-15 Published:2015-11-20

摘要/Abstract

摘要： 为探索提高石煤中钒的浸出效率，以湖北通山某石煤矿石为研究对象，进行了石煤焙烧—加压酸浸提钒工艺研究。结果表明：在焙烧温度为850 ℃、焙烧时间为60 min、釜内压力为1.0 MPa、硫酸初始浓度为15%、液固比为1.5 mL/g、浸出温度为150 ℃、浸出时间为120 min条件下，钒浸出率可达80.51%。采用红外光谱法分析了加压浸出前后云母矿物的晶体结构，并从动力学的角度揭示了浸出温度对钒浸出的影响机理。结果表明：加压浸出可以破坏云母晶格，进而有利于释放云母晶格中的钒，提高钒浸出效果。浸出过程动力学分析结果表明：浸出温度对浸出过程影响显著，浸出温度为60~120 ℃时，表观活化能为41.603 kJ/mol，浸出过程受化学反应控制；150~210 ℃时，表观活化能为4.319 kJ/mol，浸出过程受内扩散控制；加压浸出能够将浸出温度提高至100 ℃以上，有效提高了硫酸破坏云母晶格的速率，是提高钒浸出效率的关键。

关键词: 加压酸浸, 石煤, 提钒, 动力学

Abstract: In order to find a process which could increase the leaching velocity of vanadium，roasting-pressure acid leaching of vanadium on stone coal from Tongshan in Hubei was investigated.Results showed that，the optimal operation conditions are as followed:the roasting temperature was 850 ℃，the roasting time was 60 min，the kettle pressure was 1.0 MPa，initial concentration of sulfuric acid was 15%，ratio of liquid to solid was 1.5 mL/g，leaching temperature was 150 ℃ and leaching time was 120 min，with these conditions the vanadium leaching rate could reach 80.51%.The changes of mica mineral structure during leaching process were analyzed by Infrared Spectrometry analysis and the effect of temperature on vanadium efficiency was studied from the aspect of leaching kinetics.The results indicated that pressure acid leaching could destruct the crystal lattice of mica that was helpful for the release of vanadium and the increase of vanadium leaching efficiency.The leaching kinetics analysis results indicated that:effect of leaching temperature on vanadium efficiency was conspicuous，when the leaching temperature ranged from 60 to 120 ℃，the apparent activation energy was 41.603 kJ/mol and the leaching was controlled by surface chemical reaction.When the temperature ranged from 150 to 210 ℃，the apparent activation energy was 4.319 kJ/mol and the leaching was controlled by inner diffusion of reactants.As pressure acid leaching could raise the leaching temperature over 100 ℃，the destruction velocity of mica crystal lattice could be raised effectively and the vanadium leaching time could be shorten effectively.

Key words: Pressure acid leaching, Stone coal, Vanadium extraction, Kinetics

黄俊1, 张一敏, 黄晶, 刘涛, 薛楠楠. 石煤焙烧—加压酸浸提钒研究[J]. 金属矿山, 2015, 44(10): 85-89.

HUANG Jun-1, ZHANG Yi-Min, HUANG Jing, LIU Tao, XUE Nan-Nan. Study on Roasting-Pressure Acid Leaching of Vanadium from Stone Coal[J]. Metal Mine, 2015, 44(10): 85-89.

[1]	范　威, 水　沛, 谢传东, 高　霖. 基于Archard 模型与DEM 仿真的高压辊磨机磨损演化规律研究与优化[J]. 金属矿山, 2024, 53(6): 173-.
[2]	冯　强, 徐龙威, 刘炜炜, 赵子栋, 孙尚渠, 张　强. 考虑剪切的常规态近场动力学模型及岩体裂隙扩展演化规律研究[J]. 金属矿山, 2024, 53(2): 123-.
[3]	平　琦, 后健民, 胡　薇, 钱　明, 孙　栋. 高温循环作用含孔砂岩动态力学特性试验研究[J]. 金属矿山, 2024, 53(10): 76-.
[4]	王　震　路增祥. 矿山“ 生产冒进行为” 的演化博弈分析[J]. 金属矿山, 2024, 53(01): 269-275.
[5]	刘文宝, 丁睿, 刘文刚, 李维超, 张覃, 沈岩柏, 刘睿哲. 碱浸改性蛇纹石尾渣吸附材料的制备及其对 Cu2+的吸附性能研究[J]. 金属矿山, 2023, 52(11): 74-80.
[6]	任云鹏, 李安帅, 李旭东, 宋芳. 基于 DEM-MBD 的高压辊磨机仿真模型及应用研究[J]. 金属矿山, 2023, 52(09): 164-172.
[7]	张炜, 李腾飞, 管孝强, 周仕庆, 谭志勇, 李海斌, 王超. 浮选流体动力学关键技术研究与装备智能化发展路径[J]. 金属矿山, 2023, 52(09): 145-155.
[8]	李新玉, 袁帅, 高鹏, 王若枫, 张洪浩, 李艳军. CO 与 H₂气氛下赤铁矿还原动力学及矿相转化机理研究 #br#[J]. 金属矿山, 2023, 52(09): 83-89.
[9]	张是洲, 唐学芳, 吴勇, 张启蒙, 谢政. 典型铁氧化物对 Cu( Ⅱ )的吸附性能研究[J]. 金属矿山, 2023, 52(05): 306-313.
[10]	钟莹莹, 谢兵华, 杨学金, 王访, 高冀云, 马林转, 刘天成, 贾丽娟. 瓦斯灰协同氧催化脱硫体系中锌的浸出动力学研究[J]. 金属矿山, 2023, 52(01): 239-245.
[11]	邹凯, 肖军辉, 钟楠岚, 高德强. 低品位钒矿硫酸化焙烧—浸出提钒工艺试验研究[J]. 金属矿山, 2022, 51(09): 121-125.
[12]	高恩霞, 张春, 李悦鹏, 罗建辉, 高瑞琢, 冉金城. 磨矿方式对闪锌矿和黄铁矿浮选动力学影响研究[J]. 金属矿山, 2022, 51(09): 100-106.
[13]	从金瑶, 彭佳志, 涂博, 刘勇, 王海龙, 纪宪坤, 冯建. 六偏磷酸钠对铁尾砂絮凝沉降行为的影响及机理[J]. 金属矿山, 2022, 51(08): 138-145.
[14]	李嘉, 孙洪硕 , 祁生亮, 崔建辉, 李广文, 高泽宾, 曹兵. 磁化焙烧产品氧化动力学研究[J]. 金属矿山, 2022, 51(08): 114-118.
[15]	叶海旺, 李兴旺, 袁尔君, 雷涛. 骨料矿山爆破粉矿率控制技术研究[J]. 金属矿山, 2022, 51(07): 80-88.

扫码分享