金属矿山 ›› 2012, Vol. 41 ›› Issue (09): 87-89+102.

湖北某石煤湿法浸钒试验

危青，戴子林，李桂英，吴海鹰

广州有色金属研究院

出版日期:2012-09-15 发布日期:2012-10-09

Test on Hydrometallurgical Leaching of Vanadium from a Stone Coal in HuBei

Wei Qing，Dai Zilin，Li Guiying，Wu Haiying

Guangzhou Research Institute of Non-ferrous Metals

Online:2012-09-15 Published:2012-10-09

摘要/Abstract

摘要： 湖北某石煤矿中钒主要赋存于铝硅酸盐矿物中，单独使用硫酸浸出，钒的浸出率只有30%左右。考察了单独添加助浸剂A或B以及同时添加这2种助浸剂对钒浸出率的影响。结果表明，分别添加助浸剂A或B时，钒的浸出率均有所提高；在硫酸浓度为30%，矿石粒度为-0.178 mm，浸出温度为90 ℃，浸出时间为8 h，液固比为1∶1，助浸剂A添加量为4%、B添加量为2%的条件下，钒的浸出率可达到88.5%，为实现该矿石的全湿法提钒提供了技术保证。

关键词: 石煤钒矿, 湿法浸出, 助浸剂

Abstract: The vanadium stone-coal in Hubei mainly occurs in the aluminum silicate minerals.The vanadium leaching rate of sulfuric acid leaching is only about 30%.The study investigated the effect of aid-leaching reagent A, B or mixture of A and B on vanadium leaching rate, separately.The results showed that both aid-leaching reagent A or B enhanced the leaching rate of vanadium.The vanadium leaching rate reached 88.5% in the experimental condition that sulfuric acid concentration was 30%, stone coal particle size 0.178 mm, temperature 90 ℃, time 8h, liquid-solid ratio 1∶1, while adding the aid-leaching reagent A 4% and B 2%.The study provided a guarantee for the realization of vanadium's extraction with a hydrometallurgical separation method.

Key words: Vanadium containing stone-coal, Hydrometallurgical leaching, Aid-leaching reagent

危青, 戴子林, 李桂英, 吴海鹰. 湖北某石煤湿法浸钒试验[J]. 金属矿山, 2012, 41(09): 87-89+102.

WEI Qing, DAI Zi-Lin, LI Gui-Ying, WU Hai-Ying. Test on Hydrometallurgical Leaching of Vanadium from a Stone Coal in HuBei[J]. Metal Mine, 2012, 41(09): 87-89+102.

[1]	赵杰, 张一敏, 黄晶, 刘涛, 王非, 王一, 刘娟. 含氟助浸剂对石煤酸浸提钒的影响[J]. 金属矿山, 2013, 42(01): 90-93.
[2]	李秀敏, 张一敏, 黄晶, 刘涛. 助浸剂对攀钢钒尾渣酸浸提钒的影响[J]. 金属矿山, 2012, 41(07): 158-160+168.
[3]	杨晓, 张一敏, 黄晶, 刘涛, 付利攀, 赵杰, 刘娟. 助浸剂CX对石煤酸浸提钒效果的影响[J]. 金属矿山, 2012, 41(03): 86-89.
[4]	王洪忠. 氰化尾渣综合利用工艺分析与探讨[J]. 金属矿山, 2010, 39(09): 173-176.

扫码分享