离子型稀土矿无氨浸出研究

金属矿山 ›› 2014, Vol. 43 ›› Issue (10): 95-97.

离子型稀土矿无氨浸出研究

赖兰萍，欧阳红，伍莺，陈冬英

赣州有色冶金研究所，江西赣州 341000

出版日期:2014-10-15 发布日期:2015-05-19
基金资助:
* 科技部科研院所技术开发研究专项（编号：2012EG115017）。

No Ammonia Leaching Study of Ionic Rare-earth Ore

Lai Lanping，Ouyang Hong，Wu Ying，Chen Dongying

Ganzhou Nonferrous Metallurgy Research Institute，Ganzhou 341000，China

Online:2014-10-15 Published:2015-05-19

摘要/Abstract

摘要： 为从源头上解决离子型稀土矿以硫酸铵溶液为浸矿剂所带来的氨氮废水污染问题，以赣南某离子型稀土矿为对象，开展了离子型稀土矿无氨浸出研究。首先通过探索试验比较了硫酸钾、硫酸钠、硫酸镁、硫代硫酸钠、硝酸钠、亚硝酸钠、氯化镁及A₁、A₂、A₃、A₄、A₅与硫酸铵的浸矿效果，结果显示，A₂~A₅可取得与硫酸铵较接近的浸出率，而其他8种非硫酸铵浸矿剂的浸出率都太低。在探索试验基础上，对A₂~A5和硫酸铵进行了浸矿扩大试验，结果显示，A₂、A₃和A₅均可获得与硫酸铵近乎相同的浸出率（分别为95.25%，95.01%，95.18%和95.05%），但A₃和A₅的浸矿周期（分别为92和127 h）分别比硫酸铵的浸矿周期（58 h）增加了58.62%和118.97%，而A₂的浸矿周期（48 h）比硫酸铵的浸矿周期缩短了17.24%。进一步对A₂和硫酸铵所得浸矿扩大试验浸出液进行化学多元素分析，发现两者REO的浓度及杂质Fe、Al、Si、Ca的浓度都很接近。以上结果表明，A₂不仅可取代硫酸铵实现离子型稀土矿的无氨浸矿，而且可较大幅度地缩短浸矿周期。

关键词: 离子型稀土矿, 氨氮废水, 无氨浸矿

Abstract: In order to solve the pollution of ammonia nitrogen wastewater stemmed from ionic type rare-earth ore leaching using ammonium sulfate solution as the reagents，research on ore leaching with no ammonia is carried out with an ionic type rare-earth ore，Jiangxi，as the research object.Ore leaching efficiency of potassium sulfate，sodium sulfate，magnesium sulfate，sodium thiosulfate，sodium nitrate，sodium nitrite，magnesium chloride and A1，A2，A3，A4，A5，and ammonium sulfate are compared in exploring experiment.The results show that A2 ~ A5 can have nearly the same leaching efficiency as ammonium sulfate，and the other 8 kinds of leaching reagents has lower leaching rate.Extending leaching experiments are carried out using A2~A5 and ammonium sulfate as the leaching reagent，based on the exploring tests.The results indicated that，all of A2，A3 and A5 have nearly the same leaching rate as ammonium sulfate (95.25%，95.25%，95.01% and 95.05% respectively)，while leaching period of A3 and A5 (92，127 h respectively) are longer than that of ammonium sulfate (58 h) by 58.62% and by 118.97% respectively，while the leaching period of A2 (48 h) is shorter by 17.24%.Further chemical element analysis on leaching solution from extending test of A2 and ammonium sulfate as leaching reagent is conducted，finding that concentration of REO and impurities Fe，Al，Si，Ca is almost the same.In a word，A2 can not only replace ammonium sulfate to accomplish ore leaching of ionic type rare-earth without ammonia，but also greatly shorten the leaching period.

Key words: Ionic rare-earth ore, Ammonia nitrogen wastewater, Ore leaching with no ammonia

赖兰萍, 欧阳红, 伍莺, 陈冬英. 离子型稀土矿无氨浸出研究[J]. 金属矿山, 2014, 43(10): 95-97.

LAI Lan-Ping, 欧Yang-Hong , WU Ying, CHEN Dong-Ying. No Ammonia Leaching Study of Ionic Rare-earth Ore[J]. Metal Mine, 2014, 43(10): 95-97.

[1]	原伟泉, 匡敬忠, 胡海祥, 梁斌珺, 于明明. 离子型稀土浸出过程杂质形成与去除研究进展[J]. 金属矿山, 2024, 53(7): 119-.
[2]	胡洁, 周贺鹏, 雷梅芬, 张永兵, 罗仙平. 离子型稀土矿浸出渗流规律与调控方法研究[J]. 金属矿山, 2017, 46(07): 115-120.
[3]	鞠丽萍, 祝怡斌, 李青. 南方某离子型稀土矿山的土地复垦[J]. 金属矿山, 2015, 44(09): 161-165.
[4]	周丹, 罗才贵, 苏佳, 罗仙平1. 离子型稀土矿区土壤生态恢复[J]. 金属矿山, 2014, 43(10): 103-109.
[5]	罗才贵, 罗仙平, 苏佳, 陈春飞, 韩冬雪1. 离子型稀土矿山环境问题及其治理方法[J]. 金属矿山, 2014, 43(06): 91-96.
[6]	罗仙平, 翁存建, 徐晶, 马沛龙, 唐学昆, 池汝安. 离子型稀土矿开发技术研究进展及发展方向[J]. 金属矿山, 2014, 43(06): 83-90.
[7]	刘飞飞, 张满军, 刘宗来. 黏性矿物中刀盘扭矩及掘进总推力建模与试验研究[J]. 金属矿山, 2014, 43(04): 129-133.

扫码分享